Powdery Magnesia Alumina Ramming Mass For Metallurgy Industry
Powdery Magnesia Alumina Ramming Mass For Metallurgy Industry
Experience unparalleled quality with our factory-made Powdery Magnesia Alumina Ramming Mass for Metallurgy Industry. Trust us for all your metallurgical needs.
Magnesium ramming refractory mass is a high proportion of granular materials and a very low proportion of the binder and other groups of distribution system, and even all of the grain, powder composition, to be beaten by the way of the construction of a strong. Magnesia ramming mass is mixed by corundum, high quality bauxite clinker, silicon carbide as aggregate, all kinds of powder, ultra fine powder, micropowder, alumina powder and admixture with mixture rations according to differernt varieties.
Properties of Magnesium Ramming Mass
Low bulk density and low thermal conductivity,
High mechanical strength,
Good thermal shock resistance,
Tiny linear variation,no cracking,
Resistant to scour and erosion,abrasion,
Good volume stability under high temperature,
Easy to operate: times and labor saving.
Manufacturing Process of Magnesium Ramming Mass
Magnesia ramming mass is a kind of alkali amorphous refractory material, which is composed of electromagnet or sintered magnesia refractory materials, superfine powder additive and chemical bond. Firstly, high purity magnesia sand and magnesia powder are calcined for three times to allow full expansion and contraction of magnesia sand and magnesia powder. Then proportion of magnesia grains is made according to the formulation requirements.
Use Method of Magnesium Ramming Mass
1.Spread the material in the bottom with thichness of100mm to 150mm and rammedhard, 2.Clean the surface, repeat the ramming work once again 3.Put a piece of steel sheet on the surface to avoid damage on the surface when putting scrap and hot metal.
Rongsheng Refractory Magnesium Ramming Mass Specifications
Item
M-95
DM-90
Chem.comp≥
MgO
95
90
Cr2O3
2.0
2.0
BD g/cm3≥
2.80
2.70
110℃ strength of drying(MPa)≥
40
38
1300℃ strength after burning(MPa)≥
40
34
1600℃ strength after burning(MPa)≥
40
38
APP:Used for steel open hearth furnace foor filling material,manding of coverter and filling
Application of Magnesium Ramming Mass
Refractory magnesia ramming mass can be used as new lining or repair material, such as open hearth bottom repair, converter lining repair, or steel mouth filling material. And magnesium ramming mass also used in metallurgy, building materials, non ferrous metal smelting, chemical industry, machinery and other manufacturing industries.
Magnesium Ramming Mass Manufacturer from RS Refractory Factory
RS refractory factory is a professional refractory magnesium ramming mass supplier that established in the early 90s of twenty century. RS refractory factory has specialized in magnesium ramming mass for more than 20 years. if you have some demand of magnesium ramming refractory mass, or have some questions on magnesia ramming mass about physical and chemical indicators, please contact us for free. and Rs refractory factory as a professional refractory magnesia ramming mass manufacturer in china, has some competitive advantages as follows:
Competitive Price: Make the products competitive in your market,
Abundant Experience: Prevent cracks and twist in bricks,